50E-3 Advanced Optical Transparent Coating By XiangYang Jingxin Hui Ming Technology Co., LTD,

50E-3 Advanced Optical Transparent Coating

Prix FOB

Obtenir le dernier prix

( Negotiable )

16 Ton Minimum Order

Pays:

China

N Â° de modÃ¨le:

JXHM50E-3

Prix FOB:

( Negotiable )(Negotiable) Obtenir le dernier prix

LocalitÃ©:

Prix de commande minimale:

Commande minimale:

16 Ton

Packaging Detail:

20L iron pail or 200L iron pail

Heure de livraison:

20 to 30 days before T/T

Capacité de Fournir:

16 Ton per Month

Payment Type:

T/T

Groupe de produits :

coating

SpÃ©cification du produit

Classification: Double Components Adhesives
Main Raw Material: Acrylic
Brand Name: Xiang yang JingXinHuiMing

La description

*0E*3 Advanced Optical Transparent Coating

JXHM**0E*3 is a one-component or two-component advanced optical transparent coating.The coating is with waterproof, acid resistance, alkali and salt resistance, high temperature and low temperature properties, as well as can effectively reduce the loss of light.

Application

It is mainly applied to the surface protection of optical guide, diffuse, automotive lighting,street lamps, mirrors and aluminized film.

Technical performance index

1. Appearance: clear transparent sticky liquid

2. Viscosity(*0â„ƒ) : ***0~ ***0 mPa. s

3. Solid content(%): *8± 2%

4. pH value: *- 6.5

5. Light transmittance≥*9%

Ratio of two-component using

Main agent: Curing Agents ï¼ˆ*0% Solid content) = *0:**2

Recommended: main agent and curing agent = *0ï¼š1.5

NOTE: One-component *0E*3 without adding curing agent; its strength is slightly less than the two-component *0E*3.

Diluent

Special formulated diluents; or mixture of butyl acetate and cyclohexanone (ratio: 1:1)

Collocation method in order

Main agent ( *0 parts) + diluent ( 5 parts ~ 7 parts)= and stir completely + curing agent (0 ~ 2 parts) and stir completely again.

Cautions:

1. Drying timeï¼šIt should be immediately placed into the drying tunnel for baking after coating or spraying. 4 levels of increasing temperatures should be used:

first stage:*0~*5â„ƒ;
second stage:*0~*5â„ƒ;
third stage:*0~*0â„ƒ;
fourth stage:**0~**0â„ƒ.

It can be dried after solvent evaporated.

2. Curing time: curing at room temperature for a week, or baking at **0â„ƒ for 3 hours. It is not necessary to cure for the one-component coating.

3. Cant be mix with other coatings.

4. To avoid turbidity, please clean up other types of coating, include equipped with plastic tank,plastic buckets and all tools before using the coating.

5. The process ratio in this paper is for reference only. Due to different manufactures are with different technology conditions, raw material conditions and equipment conditions, we recommend that manufactures confirm the pre-tests or consult with us before using. Our products are only sold according to general condition.

6. According to customer demand for products, we can make the overall design of the program,including modifying the product formulation and setting the process methods.

Pays:	China
N Â° de modÃ¨le:	JXHM50E-3
Prix FOB:	( Negotiable ) (Negotiable) Obtenir le dernier prix
LocalitÃ©:	-
Prix de commande minimale:	-
Commande minimale:	16 Ton
Packaging Detail:	20L iron pail or 200L iron pail
Heure de livraison:	20 to 30 days before T/T
Capacité de Fournir:	16 Ton per Month
Payment Type:	T/T
Groupe de produits :	coating