DIN 1.***0 / X**0Cr*2 Steel is a high Carbon and high Chromium cold work tool steel. The 1.***0 steel has good hardenability and wear resistance. But due to the carbon content of X**0Cr*2 steel is high,which makes this material hard and brittle. So din 1.***0 can not afford a bigger punch load and has low impact toughness.
Chemical Composition
C: 1.***2.*0; Si: 0.***0.*0; Mn: 0.***0.*0;
P: max0.**0; S: max0.**0; Cr: *1.****3.*0;
Equivalent Grades
AISI/ASTM: D3
BS: BD3
JIS: SKD1
Russia: KH*2
Form of 1.***0
Round / Flat Bars, Plates, Blocks
Size of X**0Cr*2
Round bar
dia. ***6mm (Cold Drawn);
dia. ****0mm (Hot Rolled);
dia. *****0mm (Hot Forged);
dia. ******0mm (Free Forging);
Flat bar
Thickness: **2.5mm(Cold Rolled); 1.***0mm(Hot Rolled); *****0mm(Hot
Forged);
Width: Max**0mm;
Surface Condition of 1.***0 Steel
Black, Peeled, Rough Machined, Ground
Hardness of X**0Cr*2 Steel
Annealed (+A):
******9HB
Mechanical Properties of W-Nr 1.***0 Steel
Tensile strength
Yield point
Percentage reduction of area after fracture
Elongation after fracture
Impact test
Quenched and Tempered (+QT) of 1.***0 / X**0Cr*2
1. Heat din 1.***0 steel to the hardening temperature of
*******0°C;
2. Quench in the oil then cool down;
3. Heat uniformly to the required tempering temperature;
4. Withdraw X**0Cr*2 steel from the furnace and cool in air;
5. The general tempering temperature is **0°C which can make the
material at *0HRC.
Applications of DIN X**0Cr*2 Steel
The 1.***0 tool steel is usually used to make cold die that the
impact load is small and with high wear resistance. X**0Cr*2 steel
is also used for cold cutting blade,drill sets,gauge,drawing
die,stamping die,thread rolling plate,deep drawing die and thread
rolling die,etc.