Description
Description
HO***2 uses the chemical treatment on the non-corona surface of
BOPET and the metalized treatment on the corona surface of BOPET,
which enhances its capability of barriering water vapor and oxygen,
and its compounding and bonding functions. It is mainly applied to
the long-term storage of such articles as tea, milk powder, coffee,
cookie, chips, wheat biscuit, vitellus pie, almond crisp, savory
fillet, medicine, Dora-Yaki, ketchup, hot-pot soup base, seasoning
soft packing, solar cooker, etc.
â—High
gloss;
â—Good printability
â—Good insulating and reflecting
properties;
â—Good UV and IR resistances;
â—Good barrier property and fragrance
retentivity; â—Good health security
â—Good optical and dimensional
stabilities;
â—Good strength and stiffness, cold/heat resistances;
3. Standard Specifications
| The Thickness of the film |
The Standard Length(m) |
Adjusted Length
(times of standard) |
| *-50 um |
***0 |
1,2,3,4 |
| The Joint Qty(pc) |
One is allowed, it should be controlled
below *0% of standard film length. |
| Width |
*******0 mm |
| Roll Core Diameter ID |
3(*6.2mm) ; 6（**2.4mm） |
4. Physical and Mechanical Properties of VMCPP
| No. |
The Item |
|
Typical Values of MPET |
|
1 |
Tensile strength Mpa≥ |
MD |
**0 |
| TD |
**0 |
|
2 |
The Elongation At Break %≥ |
MD |
**0 |
| TD |
**0 |
|
3 |
The Shrinkage(**0℃,*0min) %≤ |
MD |
2 |
| TD |
1.5 **0 ℃ *0 min |
| 4 |
The Wetting Tension mN/m |
56 |
| 5 |
Adhesion of Aluminium Layer |
Excellent |
| 6 |
Thickness of Aluminium Layer Ω/â–¡; OD |
0.8*4.0Ω/â–¡ |
0.**3.5OD |
| 7 |
Uniformity of Aluminium Layer±ï¼… |
***0 |
All property indexes above are the typical data of this model, for
your reference only. Customers can put forward reasonable
requirements in thickness, uniformity, etc. of the aluminum coating
according to your demands, and indicate in your order.