Description
Stanvac Ultra Bright Zinc Spray is a quick drying, light-duty,
sacrificial coating that protects ferrous metals from oxidizing. It
Provides barrier
as well higher degree of cathodic protection to the base metal
against the
environment .and prevent the formation or spreading of rust and
corrosion. It
also provides the appearance of a high shine, hot-dip galvanized,
bright metallic
finish. Stanvac Ultra Bright Zinc Spray is excellent for touch-ups
to scratches,
dents, welds, wear or machined edges on galvanized, aluminum and
other high
shine metal substrates.
Benefits:
 High Shine Finish. A glistering coating with *5% zinc-Al in
dry film.
Provides the appearance of a hot-dip galvanized, bright metallic
finish.
 Sacrificial Zinc Coating. Stops rust & corrosion on
steel structures, equal to
Hot dipped galvanizing.
 Quick Drying. Dries to touch in *5 to *0 minutes. Allows
treated parts to be
handled quickly.
 Resistant to salt spray and weathering. Good film integrity
after **0hrs SST.
 Restors bright look of hot dipped galvanizing on damaged
surfaces.
 Excellent heat resistance in class.
 Aluminum powder gives a brighter finish to help blend with
existing coatings.
 Can be used on previously coated surfaces.
 High purity powders
 Excellent adhesion
Unique Feature:
Optimum corrosion protection was generally linked to a high zinc
content in the coating. Spherical
zinc pigments and a relatively high layer thickness formed the
basis for this corrosion protection.
However today, further developments of corrosion
protection primers based on zinc flakes enable
considerably improved corrosion protection compared to
what was possible in the past with spherical zinc dust.
The zinc flakes used in the STANVAC ULTRA BRIGHT
ZINC SPRAY have a large, specific surface geometry,
and therefore a high barrier+ Cathodic protection effect.
Even when the particles are shifted, the contact, conductivity and
cathodic corrosion protection
are maintained, as the pigments lie closely on each other in
sheets.
In addition, the long diffusion paths result in an even greater
resistance to environmental
influences.
Application:
 Recommended for use on threads, exposed edges, fasteners,
conduit, strapping,
welds, fencing, railings, grates, electrical poles, breaker panel
housings, rain spouts, signs, doors,
trailers, waste containers, catwalks and guard rails. Ideally
suited for a variety of environments
including marine, utility, refinery, water treatment, chemical
processing, pulp & paper, steel
manufacturing and general maintenance and repair.
Directions:
Surface Preparation
New Steel - Surface must be dry and free of contamination. Remove
all weld spatter and grind all
rough welds and sharp edges to a smooth contour. For severe
exposure (immersion, chemical,
etc.) near-white blast clean per SSPC SP ****3T. For other
exposures blast clean per SSPC SP
6 - *3 to a maximum profile of 1.5
Directions
 Surface should be dry and free of rust bloom.
 Shake well until agitator ball is free. Repeat while
using.
 Best results are obtained when sprayed above *0ºF. Spray
from ****5 inches away in light,
even coats.
 The optimum film thickness for Stanvac Ultra Bright Zinc is
1.5 to 3.0 mils of dry film. To obtain
this thickness via aerosol application, 3 passes of spray are
required. Spray the substrate
once vertically, once horizontally, and once more vertically for
ideal coverage.
 Additional coats for heavy film can be applied when first
coat is dry. For a thickness of 3 mils,
repeat the above spray pattern twice.
 When finished spraying, clean valve by turning can upside
down and pressing button until only
pressure escapes.
 If clogging occurs, remove button and clean slot and orifice
with fine wire.
CHARACTERISTICS AND PROPERTIES:
Appearance:
Class …………………………….. Metallic
Coverage: Aerosol
Theoretical-at 1 mil dry……………..*3 sq. ft./can
Drying Schedule: (At *7°F [*5°C], *0% Humidity at 1 mil, dry)
To touch……………………………. *0 min
To handle…………………………… *0 min
Full cure…………………………….. *2 hrs
To recoat…………………………… After *0 min.
Performance and Chemical Properties: Aerosol
Specific gravity…………………….. 0.*0 + 0.*0
Interior/ exterior durability……… Excellent
Temperature resistance (Dry) …………… *0°C Continues,
**4°C Intermittent
Adhesion …………………………… Very good
Salt spray corrosion ………………... **0 hrs
Mineral spirits resistance ………….. Good
IMPORTANT:
1. Contains no Ozone Depleting Substances (O.D.S).
2. Warranted to confirm to international ICC & DOT
regulations.
3. Minimum *2 Months performance guarantee: - Warranted against any
defect in material or a
period of *2 months from the date of supply.
CAUTION:
Proper precautions should be taken to assure operator protection,
including explosion-proof
electrical fixtures when applied indoors. Aerosol Cans do not
puncture, incinerate or store above
**0° F. Exposure to high temperatures may cause can to burst. Do
not place in direct sunlight or
near any heat source. Aerosol cans will conduct electricity. Keep
away from all live electrical
sources including battery terminals, solenoids, electrical panels