Jinan TY Refractory Co., Ltd

High Alumina Cement (CA-70, CA-80) CA-70 or CA-80 is a general pure calcium aluminate cement with an alumi

SiO2(%)>91 apparent density (%) <1.2; Bulk Density (g/cm3) <2.39 liner thermal expansion after 2 hour

Specification: AL2O3:45% Min Fe2O3:0.7%(Max) TiO2:1.3% Max Alkalinity:0.25% Max BD:2.45g/ccm min Moisture:0.5%

MgO:83% Refractoriness:37 binding time(min):2min Grain size%+0.5mm <=2 water added:25-35% binding stre

fire clay brick MgO(%) SiO2(%) Fe2O3(%) 0.5 ZrO2(%) Al2O3(%)42 CaO(%) apparent Porosity (%) 13 Refractorine

MgO:88-96% Grain size(mm)=0-5 water added:5-10% bonding method:chemical and ceramic bonding magnesia r

ceramic hollowares Detailed Product Description Hollowares are refractories consumables used for gating sys

Mg-97:97 magnesia MgO(%) 97.4 SiO2(%)1.0 Fe2O3(%) 0.5 ZrO2(%) Al2O3(%) CaO(%)1 apparent Porosity (%) 16 Ref

Isostatic Zircon Bricks ZrO2 % 65 69 Bulk Density g/cm3 4.25 4.15 Apparent Porosity % 1 9 Cold Crushing Str

Isopress Tin Bath Bottom Brick DX-2 Properties data Isopress Tin Bath Bottom Brick Al2O3(%) 38 Fe2O3(%) 0

Chemical Composition(%) 41# 36# 33# ZrO2 4O 35 32 SiO2 12.5 14 14 Al2O3 remains remains remains Na2O3 1.

Chemical Composition(%) 41# 36# 33# ZrO2 4O 35 32 SiO2 12.5 14 14 Al2O3 remains remains remains Na2O3 1.

Chemical Composition(%) FM-M FM-S FM-Z ZrO2 2.1 1.0 3.5 SiO2 17 20 16 Al2O3 78 74 76 CaO 0.2 0.2 0.2

Mold cutting machine 21pcs/time, 33times/min, size: 2750×1300×1400mm 500type vacuu

Mullite, Corundum-Mullite, Alumina Products Type: Mullite/Corundum-Mullite Properties data M-75 Al2O3(%) 75

Item high alumina brick Al2O3(%) ≥65 Refractoriness(&a

KAOLIN Clay Specification: AL2O3:45% Min Fe2O3:0.7%(Max) TiO2:1.3% Max Alkalinity:0.25% Max BD:2.45g/ccm mi

SiO2(%)>91 apparent density (%) <1.2; Bulk Density (g/cm3) <2.39 liner thermal expansion after 2 hour

Item Chrome magnesite brick MgO(%) ≥50 Cr2O3(%)

light forsterite brick MgO:55.45% Fe2O3:5.8% SiO2:33.50% BD:1.88 A.P:42.1% *****:8MPa R.U.L:1400 M