Titanium plate

La description

our company can provide you all kinds of titanium materials,such as, titanium plates, rods, tubes, wires and screws in accordance with the buyers' requirements. The product is made in our own factory,so, it is impossible for the intermediary trader to increase the price during the traing process. We ensure that our product are supplied with good quality and competitive price. Our company provids gr1,gr2,gr3,gr5,gr7,gr9,gr*2 titanium sheets.
Grade 1—Unalloyed titanium,
Grade 2—Unalloyed titanium,
 Grade 3—Unalloyed titanium,
Grade 5—Titanium alloy (6 % aluminum, 4 % vanadium),
 Grade 6—Titanium alloy (5 % aluminum, 2.5 % tin),
Grade 7—Unalloyed titanium plus 0.*2 to 0.*5 %
Grade *2—Titanium alloy (0.3 % molybdenum,
0.8 % nickel)
Minimum and maximum limits apply to tests taken both longitudinal and transverse to the direction of rolling. Mechanical properties for conditions other than annealed
or plate thickness over 1 in. (*5 mm) may be established by agreement between the manufacturer and the purchaser.
BT equals the thickness of the bend test specimen. Bend tests are not applicable to material over 0.**7 in. (4.*5 mm) in thickness.
C Material is identical to the corresponding numeric grade (that is, Grade 2H = Grade 2) except for the higher guaranteed minimum UTS, and may always be certified
as meeting the requirements of its corresponding numeric grade. Grade 2H, 7H, *6H, and *6H are intended primarily for pressure vessel use.
D The H grades were added in response to a user association request based on its study of over ***0 commercial Grade 2, 7, *6, and *6 test reports, where over *9 %
met the *8 ksi minimum UTS.
E For Grades 5, 6 and *2 the elongation on materials under 0.**5 in. (0.**5 mm) in thickness may be obtained only by negotiation.
F Elongation for continuous rolled and annealed (strip product from coil) for Grade 9 and Grade *8 shall be *2 % minimum in the longitudinal direction and 8 % minimum
in the transverse direction.
G Properties for material in the solution treated condition.
H Material is normally purchased in the solution treated condition. Therefore, properties for aged material shall be negotiated between manufacturer and purchaser.
I As agreed upon between purchaser and supplier.