PRETACK PA-95Â is an aromatic
modified C5 hydrocarbon resin with a
narrow molecular weight distribution. It is odor improved grade
with low odor, low wax cloud point. Its specific degree of
modification provides an excellent compatibility with SBS, SIS
and EVA polymers as well as with natural tackifier resins (like
terpene,rosin and its derivatives). It has high aromatic
content, especially suitable for application in SBS system
Adhesives.
Â
Key Characteristics:
• Good compatibility with SBS, SIS, EVA and other polymers
• Low Wax Cloud Point
• Good thermal resistance
• Low VOC and low odor
Â
Typical Properties
|
Property
|
Test method
|
Unit
|
Typical value
|
|
Color (50% resin solid in Toluene)
|
(ASTM D1544)
|
Ga #
|
Max5#
|
|
Softening point (Ring & Ball)
|
(ASTM E28)
|
℃
|
91-97
|
|
Melt viscosity(175℃)
|
(ASTM D3236)
|
mPa·s
|
Max 350
|
|
Wax Cloud Point (EVA/Resin/Wax=20/40/40)
|
(ETM 22-10)
|
℃
|
Max 85
|
|
Glass Transition Temperature (Tg)
|
midpoint
|
℃
|
47
|
|
Acid value
|
(ASTM D974)
|
mgKOH/g
|
Max 0.30
|
|
Specific gravity ,@********************td>
|
(ASTM D71)
|
20/20℃
|
0.92-0.99
|
Note:Â EVA=Vinyl acetate content of 27.5%(wt),
Wax=Paraffin wax at 68℃ melt point.
Â
Application
HMPSA, Solvent based PSA, Hot Melt Adhesive, Sealants.
Â
Packaging
PA-95 is available in 25kgs paper bag or 500kgs/1000kgs in bulk
bag.
GRESIN Â and its marketing affiliates shall not be
responsible for the use of this information, or of any product,
method, or apparatus mentioned, and you must make your own
determination of its suitability and completeness for your own
use, for the protection of the environment, and for the health
and safety of employees and purchasers of your products. No
warranty is made of the merchantability of fitness of any
product, and nothing herein waives any of the Seller's
conditions of sale.
Â
Storage
Inside storage is recommended and keep at temperature not
exceeding 30oC. Pelletized forms of resins may block or lump in
hot weather climates or if stored near heat sources. Resins are
prone to gradual oxidation, some more so than others. This
could result in darkening and/or it could have an adverse
effect on the solubility of the resin in organic solvents or on
its compatibility with polymers.Â